Description:

It has good comprehensive performance in the temperature range of -253 to 700 ℃, and the yield strength below 650 ℃ ranks first in deformed superalloys. Bin has good fatigue resistance, radiation resistance, oxidation resistance, corrosion resistance, and good processing properties. And long-term organizational stability, it can manufacture various parts with complex shapes. It has been widely used by the Commission for Discipline Inspection in the above-mentioned temperature range in the aerospace, nuclear energy, and petroleum industries.

 

Application field：

lAero Engine Parts

lGas turbine components

lNuclear Energy Industry Parts

lInstrument parts

lPower Engineering Components

 

 

 

 

 

Physical properties

Density: 8.5g/cm3

Specific surface area: 0.243cm2/g

Sphericity≥98.5%

Bulk density: 17.8s/50g

Hall flow rate: 17.8s/50g

Melting point: 1260-1340°C

Relative density: close to 100%

Recommended layer thickness: 15μm, 20μm, 30μm, 40μm, 50μm

 

Technical standards: ASTM B637, AMS 5662,AMS 5663,AMS 5664.

Note: If the alloy powder has moisture absorption, or the storage period exceeds 3 months, it should be used before

Carry out drying treatment (150℃, heat preservation for 2 hours)