Description:

It has good creep strength, thermal fatigue performance and oxidation resistance below 900°C. It has been used to ≤restore the organization and use performance of parts that have degraded and reduced performance after long-term use.

 

Application field：

lIndustrial high temperature parts

lGas turbine guide vane

lGas Turbine Turbine Rotor

 

 

 

 

Physical properties

Density: 8.150g/cm3

Specific surface area: 0.238cm2/g

Sphericity ≥98.5%

Bulk density: 4.05g/cm3

Hall flow rate: 18.3s/50g

Melting point: 1280-1350°C

Relative density: close to 100%

Recommended layer thickness: 15μm, 20μm, 30μm, 40μm, 50μm

 

Note: If the alloy powder has moisture absorption, or the storage period exceeds 3 months, it should be used before

Carry out drying treatment (150℃, heat preservation for 2 hours)