Description:

It has good oxidation and corrosion resistance, moderate durability and creep strength at 900°C, good cold and hot processing formability and welding performance. It is suitable for the manufacture of combustion chamber parts and other high temperature parts of aero engines. It can be used for a long time below 900℃ and the working temperature can reach 1080℃ in a short time.

 

Application field：

lIndustrial and aviation steam turbine structural parts

lIndustrial furnace parts

lSpiral tube in petrochemical furnace

lHigh temperature gas cooled nuclear reactor

 

 

 

Physical properties

Density: 8.5g/cm3

Specific surface area: 0.232cm2/g

Sphericity≥98.5%

Bulk density: 4.21g/cm3

Hall flow rate: 17.2s/50g

Melting point: 1260-1340°C

Relative density: close to 100%

Recommended layer thickness: 15μm, 20μm, 30μm, 40μm, 50μm

 

Technical standard: "Technical Specification for Hastelloy X Powder Special for 3D Printing"

Note: If the alloy powder has moisture absorption, or the storage period exceeds 3 months, it should be used before

Carry out drying treatment (150℃, heat preservation for 2 hours)