Description:

Corrosion resistant alloys with many excellent properties have good resistance to oxidizing and moderate reducing corrosion. It is one of the only materials that can withstand the corrosion of wet chlorine, hypochlorite and chlorine dioxide solution.

It has excellent resistance to stress corrosion cracking and good local corrosion resistance. It has satisfactory corrosion resistance in many chemical process media, including strong etched inorganic acid solutions. Chlorine and various media containing chlorides, dry chlorine, formic acid, acetic acid, sea water and salt water, etc.

 

Application field：

Nuclear energy industry, chemical treatment, pollution prevention

lEvaporator in chemical and petroleum industry

lReactor for acetic acid and acid products

lHeat exchanger, reactor

lEquipment and components operating in an acid gas environment

lSulfuric acid condenser

 

 

Physical properties

Density: 8.90g/cm3

Specific surface area: 0.253cm2/g

Sphericity ≥98.5%

Bulk density: 4.55g/cm3

Hall flow rate: 16.7/50g

Melting point: 1325-1380℃

Relative density: close to 100%

Recommended layer thickness: 15μm, 20μm, 30μm, 40μm, 50μm

 

Note: If the alloy powder has moisture absorption, or the storage period exceeds 3 months, it should be used before

Carry out drying treatment (150℃, heat preservation for 2 hours)