Description:

Among the existing soft magnetic materials, the alloy has the highest saturation magnetic induction (2.4T), the Curie point is also high (980℃), and the saturation magnetostriction coefficient is the largest (60~100-10-6). Due to the saturation magnetic induction High, when making motors of the same power, the volume can be greatly reduced, and when making electromagnets, it can produce a large attracting force under the same cross-sectional area. Due to the high Curie point, the alloy can work at a higher temperature where other soft magnetic materials have been completely demagnetized, and maintain good magnetic stability.

 

Application field：

lAviation and aerospace parts

lMicro motor rotor, electromagnet pole head, relay, transducer, etc.

lMagnetic shielding parts

 

 

 

 

 

Physical properties

Density: 8.20g/cm3

Specific surface area: 0.232cm2/g

Sphericity ≥98.5%

Bulk density: 4.11g/cm3

Hall flow rate: 19.8s/50g

Melting point: 1350-1420℃

Relative density: close to 100%

Recommended layer thickness: 15μm, 20μm, 30μm, 40μm, 50μm,

 

Technical standard: "Technical Specification for Hiperco50 Powder Special for 3D Printing"

Note: If the alloy powder has moisture absorption, or the storage period exceeds 3 months, it should be used before

 

Carry out drying treatment (150℃, heat preservation for 2 hours)