Description:

It has high strength, high hardness and strong corrosion resistance. After heat treatment, the mechanical properties of the product are more perfect, and the compressive strength can reach as high as 1100-1300Mpa (160-190 ksi). It cannot be used at temperatures higher than 300°C (572°F) or very low temperatures. It has good corrosion resistance to the atmosphere and diluted acids or salts, and has corrosion resistance in petrochemical, food processing and paper industries.

 

Application field：

lHelicopter deck

lfood industry

lPulp and Paper Industry

lAerospace (turbine blades)

lmechanical part

 

 

 

 

 

 

Physical properties

Density: 7.9g/cm3

Specific surface area: 0.196cm2/g

Sphericity ≥98.5%

Bulk density: 3.87g/cm3

Hall flow rate: 23.7s/50g

Melting point: 1400-1440℃

Relative density: close to 100%

Recommended layer thickness: 15μm, 20μm, 30μm, 40μm, 50μm

 

Technical standard: ASTM A693,AMS 5604

Note: If the alloy powder has moisture absorption, or the storage period exceeds 3 months, it should be used before

Carry out drying treatment (150℃, heat preservation for 2 hours)