Description:

HAYNES 25 (L605) is a non-magnetic cobalt based superalloy. HAYNES 25 (L605) maintains good strength upto 2150°F. AMS 5759 requires minimum yield strength of 45,000 psi at room temperature. HAYNES 25 (L605) maintains good oxidation resistance up to 1900° F. HAYNES 25 (L605) has a unique ability to resist corrosion in very severe environments. Highly resistant to hydrochloric acid, nitric acid and wet chlorine (subject to need for exercising care in its selection at certain con¬centrations and temperatures)

 

Application field：

lHS25 is useful in gas turbine applications such as rings, blades and combustion chamber parts (sheet fabrications) and can also can be used in industrial furnace applications such as muffles or liners in high temperature kilns.

lHS25 also used in the hot sections of aircrafts, parts for gas turbine engines, bearings, springs, and heart valve.

 

 

Technical standard: AMS 5537

Note: If the alloy powder has moisture absorption, or the storage period exceeds 3 months, it should be used before

Carry out drying treatment (150℃, heat preservation for 2 hours)